Durchmesser / Lieferform
|
Durchmesser |
50 lb Bag |
|---|---|
| Flux | ED019587 |
DETAILS
Eigenschaften
- Features fast follow characteristics that allow for uniform welds at high speeds without undercut or voids
- Recommended for high speed, limited pass welding on clean plate and sheet steel
- Good wetting action
- Actual (Type 3.1) certificates for each lot of flux showing chemical composition, particle size and moisture level are available in the certificate center of lincolnelectric.com
- Mild Steel Lincolnweld® L-50®, L-60, and L-61® Low Alloy Steel Lincolnweld® L-70
Typische Anwendungen
- Single pass welding – on clean plate and sheet metal up to 4.8 mm (3/16 in) in thickness
- Hot water tanks, metal buildings and other applications requiring high speed welds
Besondere Eigenschaften
- Basicity Index: 0.8 Density: 1.5 g/cm3
Service Informationen
Dokumentation
Ergänzende Produkte
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS-Suchseite
MECHANICAL PROPERTIES
| Wire | Classification | Postweld Heat Treatment |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -20°C (0°F) |
|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A0-EM13K-H8 | As-welded | 530 (76) | 630 (92) | 27 | 73 (54) |
| Lincolnweld® L-60 | F7A0-EL12 | As-welded | 420 (60) | 520 (75) | 31 | 87 (64) |
| Lincolnweld® L-61® | F7A0-EM12K | As-welded | 480 (70) | 580 (84) | 28 | 69 (51) |
| Lincolnweld® L-70 | F9A0-EA1-G | As-welded | 570 (82) | 650 (95) | 26 | 56 (41) |
| Wire | Classification | Postweld Heat Treatment |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -20°C (0°F) |
|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A0-EM13K-H8 | As-welded | 530 (76) | 630 (92) | 27 | 73 (54) |
| Lincolnweld® L-60 | F7A0-EL12 | As-welded | 420 (60) | 520 (75) | 31 | 87 (64) |
| Lincolnweld® L-61® | F7A0-EM12K | As-welded | 480 (70) | 580 (84) | 28 | 69 (51) |
| Lincolnweld® L-70 | F9A0-EA1-G | As-welded | 570 (82) | 650 (95) | 26 | 56 (41) |
DEPOSIT COMPOSITION
| Wire | Classification | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si |
Diffusible Hydrogen
mL/100g Weld Metal |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A0-EM13K-H8 | 0.05 | 0.14 | 1.05 | 0.022 | 0.006 | 1.05 | 5 | |||
| Lincolnweld® L-60 | F7A0-EL12 | 0.06 | 0.11 | 1.04 | 0.017 | 0.008 | 0.73 | ||||
| Lincolnweld® L-61® | F7A0-EM12K | 0.04 | 0.06 | 1.52 | 0.020 | 0.008 | 0.97 | ||||
| Lincolnweld® L-70 | F9A0-EA1-G | 0.06 | 0.04 | 0.08 | 1.40 | 0.51 | 0.04 | 0.018 | 0.009 | 0.83 |
| Wire | Classification | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si |
Diffusible Hydrogen
mL/100g Weld Metal |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A0-EM13K-H8 | 0.05 | 0.14 | 1.05 | 0.022 | 0.006 | 1.05 | 5 | |||
| Lincolnweld® L-60 | F7A0-EL12 | 0.06 | 0.11 | 1.04 | 0.017 | 0.008 | 0.73 | ||||
| Lincolnweld® L-61® | F7A0-EM12K | 0.04 | 0.06 | 1.52 | 0.020 | 0.008 | 0.97 | ||||
| Lincolnweld® L-70 | F9A0-EA1-G | 0.06 | 0.04 | 0.08 | 1.40 | 0.51 | 0.04 | 0.018 | 0.009 | 0.83 |
FLUX COMPOSITION
| Classification | %Al2O3 | %CaF2 | %CaO | %MgO | %MnO | %Na2O | %SiO2 | %TiO2 | %ZrO2 | %Metal Alloys |
|---|---|---|---|---|---|---|---|---|---|---|
| Typical Result | 4 | 5 | 1 | 13 | 15 | 2 | 26 | 10 | 19 | 3 |
| Classification | %Al2O3 | %CaF2 | %CaO | %MgO | %MnO | %Na2O | %SiO2 | %TiO2 | %ZrO2 | %Metal Alloys |
|---|---|---|---|---|---|---|---|---|---|---|
| Typical Result | 4 | 5 | 1 | 13 | 15 | 2 | 26 | 10 | 19 | 3 |