Lincore® 15CrMn

Schweißen mit selbstschützenden Fülldrähten (FCAW-S) | ED031126

KLASSIFIZIERUNGEN::
EN ISO : T Fe9

LINCORE® 15CRMN Wire for spreader cones, crusher hammers, and manganese parts. Use as a build-up layer before capping with abrasion-resistant alloys.

Durchmesser

Durchmesser wählen

  • 2,8 mm
  • 2.0 mm

Lieferform

Lieferform auswählen

  • 11.3 KG SPOOL

DETAILS

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Eigenschaften

  • Geeignet zum schutzgaslosen Schweißen austenitischer Manganstähle mit unlegierten, niedriglegierten, austenitischen und korrosionsbeständigen Stählen
  • Unbegrenzte Lagenanzahl mit entsprechender Vorwärmung und Zwischenlagentemperatur
  • Geeignet für Pufferlagen unter Hartauftragungen
  • Unlimited layers with proper preheat and interpass temperatures and procedures
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Service Informationen

Dokumentation

Ergänzende Produkte

50lb Coil Ultracore 70C

Lincore® 15CrMn

ED022061

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS-Suchseite

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.