CHROMET® 1X

Stick (SMAW)

CLASSIFICATIONS:
AWS A5.5 : E8018-B2 H4R
EN ISO 3580-A : E CrMo1 B 3 2 H5
EN ISO 3580-B : E 5516-1CM

B2 alloyed steel designed for prolonged elevated temperature service up to 550°C

Diameter

Select Diameter

  • 2.5x350 mm
  • 3.2x350 mm
  • 4.0x450 mm

Package

Select Package

  • CAN 11.7 KG (3 x 3.9 KG, approx. 495 pcs)
  • CAN 12.3 KG (3 x 4.1 KG, approx. 330 pcs)
  • CAN 16.5 KG (3 x 5.5 KG, approx. 243 pcs)
  • VPMD 11,4 KG (6 x 1,9 KG, approx. 480 pcs)
  • VPMD 12 KG (6 x 2 KG, approx. 330 pcs)

DETAILS

Stick electrode – 1¼Cr-½Mo deposit which meets specific requirements for improved temper embrittlement resistance with prolonged service at 400-600°C.

Features

  • 1¼Cr-½Mo deposit which meets specific requirements for improved embrittlement resistance after prolonged service at 400-600°C
  • Relevant trace elements (P, Sn, As, Sb) are controlled to ensure low Bruscato (X) and Watanabe (J) factors
  • Basic flux, metal powder type coatings on low carbon high purity core wire
  • Recovery is about 115%

Typical Applications

  • Petro-Chemical
  • Power Plants
  • Piping
  • Turbine Casting
  • Boiler Superheaters

Welding Positions

  • All position, except vertical down

Service Information

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.5 E8018-B2 H4R
ISO ISO 3580-A E CrMo1 B 3 2 H5
ISO ISO 3580-B E 5516-1CM

MECHANICAL PROPERTIES

Classification Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
%
E8018-B2 H4R Requirement 460 (67) min. 550 (80) min. 19 min.
E CrMo1 B 3 2 H5 Requirement 355 (51) min. 510 (74) min. 20 min.
E 5516-1CM Requirement 460 (67) min. 550 (80) min. 17 min.
Typical Result, Stress relieved 520 (76) 610 (88) 25

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Mo %Nb %Ni %P %S %Si %Total Cu
E8018-B2 H4R Requirement 0.05 - 0.12 1.00 - 1.50 0.90 max. 0.40 - 0.65 0.03 max. 0.03 max. 0.80 max.
E CrMo1 B 3 2 H5 Requirement 0.05 - 0.12 0.90 - 1.40 0.40 - 1.50 0.45 - 0.70 0.01 max. 0.3 max. 0.030 max. 0.025 max. 0.80 max. 0.3 max.
E 5516-1CM Requirement 0.05 - 0.12 1.00 - 1.50 0.90 max. 0.40 - 0.65 0.030 max. 0.030 max. 0.80 max.
Typical Result 0.06 1.25 0.70 0.55 0.00 0.1 max. 0.009 0.012 0.25 0.0 max.

TYPICAL OPERATING PROCEDURES

Diameter Current
Amps
2.5 mm (3/32") 70-110
3.2 mm (1/8") 80-140
4.0 mm (5/32") 100-180
5.0 mm 140-240