Détails
Traits
- Easy strike
- Premium arc performance
- Easy slag removal
Applications typiques
- Low temperature applications
- Refrigerated ammonia tanks
- Liquefied gas storage, piping and transportation
- Weathering steels
- Applications requiring stress-relieved conditions
Positions de soudage
- All except vertical down
Gaz de protection
- Not Applicable
Caractéristiques spéciales
- Designed to produce a nominal 2.25% nickel deposit
Disclaimers
Des informations de service
Vous pourriez également avoir besoin
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.5 | E8018-C1 H4R |
| CWB | CSA W48 | E5518-C1-H4 |
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.5 | E8018-C1 H4R |
| CWB | CSA W48 | E5518-C1-H4 |
MECHANICAL PROPERTIES
| Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -60°C (-75°F) |
Hardness Rockwell B |
|---|---|---|---|---|---|
| E8018-C1 H4R Requirement | 460 (67) min. | 550 (80) min. | 19 min. | 27 (20) min. | |
| Typical Result, 1 hour @ 605°C (1125°F) | 460-560 (67-81) | 560-660 (82-96) | 23-30 | 50-138 (37-102) | 88-94 |
| Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -60°C (-75°F) |
Hardness Rockwell B |
|---|---|---|---|---|---|
| E8018-C1 H4R Requirement | 460 (67) min. | 550 (80) min. | 19 min. | 27 (20) min. | |
| Typical Result, 1 hour @ 605°C (1125°F) | 460-560 (67-81) | 560-660 (82-96) | 23-30 | 50-138 (37-102) | 88-94 |
DEPOSIT COMPOSITION
| Classification | %C | %Mn | %Ni | %P | %S | %Si |
Diffusible Hydrogen
mL/100g Weld Metal |
1800F H2O - As received | 1800F H2O - After 9 hrs at 80F/80%RH |
|---|---|---|---|---|---|---|---|---|---|
| E8018-C1 H4R Requirement | 0.12 max. | 1.25 max. | 2.00 - 2.75 | 0.03 max. | 0.03 max. | 0.80 max. | 4 max. | 0.2 max. | 0.4 max. |
| Typical Result | 0.05-0.11 | 0.92-1.22 | 2.04-2.35 | 0.01-0.02 | 0.01 max. | 0.23-0.38 | 1-4 | 0.2 max. | 0.1-0.4 |
| Classification | %C | %Mn | %Ni | %P | %S | %Si |
Diffusible Hydrogen
mL/100g Weld Metal |
1800F H2O - As received | 1800F H2O - After 9 hrs at 80F/80%RH |
|---|---|---|---|---|---|---|---|---|---|
| E8018-C1 H4R Requirement | 0.12 max. | 1.25 max. | 2.00 - 2.75 | 0.03 max. | 0.03 max. | 0.80 max. | 4 max. | 0.2 max. | 0.4 max. |
| Typical Result | 0.05-0.11 | 0.92-1.22 | 2.04-2.35 | 0.01-0.02 | 0.01 max. | 0.23-0.38 | 1-4 | 0.2 max. | 0.1-0.4 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity⁽¹⁾ |
Current
Amps |
|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 70-110 |
| 3/32 in (2.4 mm) | AC | 80-120 |
| 1/8 in (3.2 mm) | DC+ | 90-160 |
| 1/8 in (3.2 mm) | AC | 100-160 |
| 5/32 in (4.0 mm) | DC+ | 130-210 |
| 5/32 in (4.0 mm) | AC | 140-210 |
| 3/16 in (4.8 mm) | DC+ | 180-300 |
| 3/16 in (4.8 mm) | AC | 200-300 |
| 7/32 in (5.6 mm) | DC+ | 250-330 |
| 7/32 in (5.6 mm) | AC | 270-370 |
| 1/4 in (6.4 mm) | DC+ | 300-400 |
| 1/4 in (6.4 mm) | AC | 325-430 |
| Diameter | Polarity⁽¹⁾ |
Current
Amps |
|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 70-110 |
| 3/32 in (2.4 mm) | AC | 80-120 |
| 1/8 in (3.2 mm) | DC+ | 90-160 |
| 1/8 in (3.2 mm) | AC | 100-160 |
| 5/32 in (4.0 mm) | DC+ | 130-210 |
| 5/32 in (4.0 mm) | AC | 140-210 |
| 3/16 in (4.8 mm) | DC+ | 180-300 |
| 3/16 in (4.8 mm) | AC | 200-300 |
| 7/32 in (5.6 mm) | DC+ | 250-330 |
| 7/32 in (5.6 mm) | AC | 270-370 |
| 1/4 in (6.4 mm) | DC+ | 300-400 |
| 1/4 in (6.4 mm) | AC | 325-430 |
NOTES
| Note |
|---|
| ⁽¹⁾ Preferred polarity is listed first. |