Hardfacing Consumables Family Group

Diameters / Packaging

Diameters
 11.3 KG SPOOL
0.045 in (1.1 mm) ED031128
1.6 mm ED031129
2.0 mm ED031130

Lincore® M

Flux-Cored Self-Shielded (FCAW-S)

CLASSIFICATIONS:
EN ISO : T Fe9

LINCORE® M Wire produces manganese deposits on hammers, dredge parts, and buckets.

Diameter

Select Diameter

  • 0.045 in (1.1 mm)
  • 1.6 mm
  • 2.0 mm

Package

Select Package

  • 11.3 KG SPOOL

DETAILS

LINCORE® M ideal for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels, deposits resistance on severe impact as well as moderate abrasion and offers unlimited layers with proper preheat and interpass temperatures and procedures.

Features

  • Deposit resists severe impact as well as moderate abrasion
  • Produces an austenitic manganese deposit that work-hardens
  • Recommended for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Typical Applications

  • Hammers
  • Dredge parts
  • Crushers
  • Breaker bars
  • Buckets

Welding Positions

  • Flat

Service Information

You May Also Need

33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031129
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031130
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M Flux-Cored (FCAW-S) Wire

ED031128

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-28
Typical Result, Work-hardened 30-48

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Ni %Si
Typical Result 0.6 4.9 13.0 0.5 0.4

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 25 (1) 5.1 (200) 22 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 25 (1) 8.9 (350) 24 145 2.7 (6.0)
0.045 in (1.1 mm) DC+ 25 (1) 12.7 (500) 26 185 4.4 (9.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 3.8 (150) 23 130 2.2 (4.9)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 6.4 (250) 25 200 3.9 (8.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 8.9 (350) 27 250 5.6 (12.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 24 240 2.9 (6.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 4.4 (175) 27 300 4.2 (9.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 29 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 25 240 3.5 (7.8)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 27 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 28 395 7.5 (16.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 1.9 (75) 25 240 3.6 (8.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 400 8.8 (19.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 32 455 11.6 (25.6)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.