Wearshield SMAW 10 Pound Carton

Diameters / Packaging

Diameters
 10 lb (4.5 kg) Plastic Tube
1/8 x 14 in (3.2 x 350 mm) ED022010
3/16 x 14 in (4.8 x 350 mm) ED022012
5/32 x 14 in (4.0 x 350 mm) ED022011

Wearshield® 60 Stick (SMAW) Electrode

Stick (SMAW) | ED022010

WEARSHIELD® 60 stick electrode is ideal for extreme abrasion hardfacing applications such as conveyor screws, brick and coke machinery, grader blades and crusher rolls/plates/jaws (Metal-to-Earth (Earth Cutting & Digging) for Extreme Abrasion and Low to Moderate Impact)

Diameter

Select Diameter

  • 1/8 x 14 in (3.2 x 350 mm)
  • 3/16 x 14 in (4.8 x 350 mm)
  • 5/32 x 14 in (4.0 x 350 mm)

Package

Select Package

  • 10 lb (4.5 kg) Plastic Tube

DETAILS

WEARSHIELD® 60 stick electrode is ideal for extreme abrasion hardfacing applications but is limited to two layers. Typical applications include conveyor screws, brick and coke machinery, grader blades and crusher rolls/plates/jaws. It can be welded in flat & horizontal positions.

Features

  • Designed to resist severe abrasion
  • It exhibits higher alloy and higher abrasion resistance than Wearshield® ABR, Wearshield® 44 or Wearshield® ME
  • Can be used on carbon, low alloy, stainless, and manganese steels
  • Deposits consist of primary carbides in a matrix of austenite-carbide eutectic
  • Deposits should be limited to two layers

Service Information

You May Also Need

Wearshield SMAW 10 Pound Carton

Wearshield® BU Stick (SMAW) Electrode

ED021991
Wearshield SMAW 10 Pound Carton

Wearshield® 60 Stick (SMAW) Electrode

ED022011
Wearshield SMAW 10 Pound Carton

Wearshield® 60

ED022012
Red Line Traditional MIG Stick Welding Gloves

Traditional MIG Stick Welding Gloves

K2979-ALL

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C
Typical Result 1 Layer 57-60
Typical Result 2 Layers 60-62

DEPOSIT COMPOSITION

Classification Number of layer %C %Cr %Mn %Mo %Si %V
Typical Result 2 Layers 5.0 23.0 0.8 2.3 1.0 0.6

TYPICAL OPERATING PROCEDURES

Diameter Polarity⁽¹⁾ Current
Amps
1/8 in (3.2 mm) DC+ 100 - 140
1/8 in (3.2 mm) AC 110 - 150
5/32 in (4.0 mm) DC+ 130 - 180
5/32 in (4.0 mm) AC 140 - 200
3/16 in (4.8 mm) DC+ 210 - 250
3/16 in (4.8 mm) AC 230 - 270

NOTES

Note
⁽¹⁾ Preferred polarity is listed first.
NOTE: The deposit is not machinable or forgeable. Cooling rate does not significantly influence abrasion resistance. Deposit will usually cross check.
If more than two-layer build-up is required, use Wearshield® 15CrMn (preferred), Wearshield® BU or Wearshield® BU30 for the preliminary layer or layers under Wearshield® 60.
On manganese steel, use Wearshield® Mangjet® or Wearshield® 15CrMn as build-up.
Preheat is not generally necessary except to be sure that work is in room temperature range 25° - 45°C (75° - 100°F).
However, preheat of 120° - 200°C (250° - 400°F) may be necessary to prevent heat affected zone cracking on high carbon steel or low alloy steel base metals.
If more than two layers must be used, or if cross checks must be eliminated, preheat to 650°C (1200°F).
Prolonged or repeated heating of manganese steel base metal over 260°C (500°F) can cause embrittlement and spalling.
Avoid base metal embrittlement by: • Limiting the temperature 260°C (500°F) at distances of 13 mm (1/2 in) away from the weld. • Minimizing the time at elevated temperatures.
The correct welding technique is a vertical electrode with a 3.2 - 4.8 mm (1/8 - 3/16 in) arc length. The large ball on the end of the electrode should never touch the puddle. This technique will give a smooth transfer, low spatter and smooth bead.