33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Diameters / Packaging

Diameters
 25 lb (11.3 kg) Steel Spool
 33 lb (15 kg) Steel Spool
 50 lb (22.7kg) Coil
 125 lb (56.7 kg) Speed-Feed® Drum
1/16 in (1.6 mm) ED037492
5/64 in (2.0 mm) ED031126 ED022060
7/64 in (2.8 mm) ED022061 ED022068

Lincore® 15CrMn

Flux-Cored Self-Shielded (FCAW-S) | ED031126

AWS:
EN/ISO : T Fe9

LINCORE® 15CRMN Flux-Cored Self-Shielded Wire designed for spreader cones, crusher hammers and austenitic manganese parts applications and can be used as a build-up layer before capping with abrasion resistant alloys (Build Up and Joining)

Diamètre

Sélectionnez le diamètre

  • 1/16 in (1.6 mm)
  • 5/64 in (2.0 mm)
  • 7/64 in (2.8 mm)

Paquet

Sélectionnez un forfait

  • 25 lb (11.3 kg) Steel Spool
  • 50 lb (22.7kg) Coil
Acheter maintenant

Détails

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Traits

  • Provides an austenitic manganese deposit which exhibits very good crack resistance
  • Work-hardens for overlay or joining austenitic manganese steel to itself or to carbon steel
  • Can be used as a build-up layer before capping with abrasion resistant alloys
  • Can be used in open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Des informations de service

Vous pourriez également avoir besoin

50lb Coil Ultracore 70C

Lincore® 15CrMn

ED022061
SHADOW SPLIT LEATHER-SLEEVED JACKET

Shadow Split Leather Sleeved Welding Jacket - Large

K2986-L

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.