33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Diameters / Packaging

Diameters
 25 lb (11.3 kg) Steel Spool
 50 lb (22.7kg) Coil
 125 lb (56.7 kg) Speed-Feed® Drum
0.045 in (1.1 mm) ED031128
1/16 in (1.6 mm) ED031129
5/64 in (2.0 mm) ED031130 ED011160
7/64 in (2.8 mm) ED011164 ED011163

Lincore® M Flux-Cored (FCAW-S) Wire

Flux-Cored Self-Shielded (FCAW-S) | ED031128

AWS:
EN/ISO : T Fe9

LINCORE® M Flux-Cored Self-Shielded Wire produces an austenitic manganese deposit on hammers, dredge parts, crushers, breaker bars and buckets applications. (Build Up and Joining)

Diamètre

Sélectionnez le diamètre

  • 0.045 in (1.1 mm)
  • 1/16 in (1.6 mm)
  • 5/64 in (2.0 mm)
  • 7/64 in (2.8 mm)

Paquet

Sélectionnez un forfait

  • 25 lb (11.3 kg) Steel Spool
Acheter maintenant

Détails

LINCORE® M ideal for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels, deposits resistance on severe impact as well as moderate abrasion and offers unlimited layers with proper preheat and interpass temperatures and procedures.

Traits

  • Deposit resists severe impact as well as moderate abrasion
  • Produces an austenitic manganese deposit that work-hardens
  • Recommended for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Des informations de service

Vous pourriez également avoir besoin

50lb Coil Ultracore 70C

Lincore® M Flux-Cored (FCAW-S) Wire

ED011160
50lb Coil Ultracore 70C

Lincore® M Flux-Cored (FCAW-S) Wire

ED011164
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031129
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031130
Voir tout

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-28
Typical Result, Work-hardened 30-48

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Ni %Si
Typical Result 0.6 4.9 13.0 0.5 0.4

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 25 (1) 5.1 (200) 22 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 25 (1) 8.9 (350) 24 145 2.7 (6.0)
0.045 in (1.1 mm) DC+ 25 (1) 12.7 (500) 26 185 4.4 (9.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 3.8 (150) 23 130 2.2 (4.9)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 6.4 (250) 25 200 3.9 (8.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 8.9 (350) 27 250 5.6 (12.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 24 240 2.9 (6.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 4.4 (175) 27 300 4.2 (9.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 29 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 25 240 3.5 (7.8)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 27 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 28 395 7.5 (16.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 1.9 (75) 25 240 3.6 (8.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 400 8.8 (19.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 32 455 11.6 (25.6)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.