Lincore® 15CrMn Flux-Cored (FCAW-S) Wire

Saldatura con fili animati autoprotetti (FCAW-S) | ED037492

CLASSIFICAZIONI:
EN ISO : T Fe9

LINCORE® 15CRMN Flux-Cored Self-Shielded Wire designed for spreader cones, crusher hammers and austenitic manganese parts applications and can be used as a build-up layer before capping with abrasion resistant alloys (Build Up and Joining)

Diametro

Selezionare diametro

  • 1,6 mm (1/16 in)
  • 2,8 mm
  • 2.0 mm

Imballo

Seleziona imballo

  • 15 KG BOX

DETTAGLI

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Caratteristiche

  • Può essere utilizzato in modalità ad arco aperto per saldare l'acciaio austenitico al manganese con acciaio al carbonio, acciaio basso legato, austenitico o acciaio inossidabile
  • Strati illimitati grazie procedure e temperature di preriscaldo e interpass adeguate
  • Può essere utilizzato come strato cuscinetto prima del rivestimento con leghe resistenti all'abrasione
  • Unlimited layers with proper preheat and interpass temperatures and procedures
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Informazioni sui servizi

Documentazione

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina di ricerca SDS

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.